عنوان انگلیسی Delamination Wear Mechanism in Gray Cast Irons
چکیده انگلیسی مقاله An investigation of the friction and sliding wear of gray cast iron against chromium plated cast irons was carried out on a newly constructed reciprocating friction and wear tester. The tests were the first to be done on the test rig under dry conditions and at the speed of 170 cm/min, and variable loads of 20-260 N for a duration of 15 min. to 3 hours. The gray cast iron surfaces worn by a process of plastic deformation at the subsurface, crack nucleation, and crack growth leading to formation of plate like debris and therefore the delamination theory applies. No evidence of adhesion was observed. This could be due to formation of oxides on the wear surface which prevent adhesion. Channel type chromium plating 'picked' up cast iron from the counterbody surfaces by mechanically trapping cast iron debris on and within the cracks. The removal of the plated chromium left a pitted surface on the cast iron.
کلیدواژه‌های انگلیسی مقاله Wear, Delamination Wear, Gray Cast Iron, Chromium Plating

نویسندگان مقاله M. Salehi |
Mathematics, Isfahan University of Technology


نشانی اینترنتی http://www.ije.ir/article_71248_1ff9a110eda041da50b78226f7d9b8cc.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2417333.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات