Effect of Chromium Content on Formation of (Mo1-x-Crx) Si2 Nanocomposite Powders via Mechanical Alloying |
|
چکیده انگلیسی مقاله |
(Mo1-x-Crx)Si2 composite powders were successfully synthesized by ball milling of Mo, Cr and Si elemental powders. Effects of the Cr content, milling time and annealing temperature were investigated. X-ray diffraction (XRD) was used to characterize the milled and annealed powders. The morphological and microstructural evolutions were studied by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results showed that this composite formed after 20 h of milling. Increasing Cr content from 0.1 to 0.25 or 0.4 at.% changed the polymorph of synthesized MoSi2 from to as well as the formation reaction mechanism from mechanically induced self sustaining reaction (MSR) to gradual. Annealing of the milled powders led to the formation of -MoSi2 in all Cr contents. An average grain size of less than 40 nm was obtained for all Cr contents at the end of milling. In spite of grain growth and strain release during annealing, these nanocomposites remained in their nanocrystalline nature. |
|
کلیدواژههای انگلیسی مقاله |
Keywords nanocomposite, Silicides, mechanical alloying |
|
نویسندگان مقاله |
S.Ali Mirvakili | Ceramic, Materials and Energy Research Center, Tehran, Iran
Mohammad Zakeri | , Merc
Rahim Yazdani Rad | Semiconductor, Materials and Energy Research Center, Tehran, Iran
|
|
نشانی اینترنتی |
http://www.ije.ir/article_71979_85fac9b1c13b8e1a7bfe761912d8346e.pdf |
فایل مقاله |
اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2063032.pdf |
کد مقاله (doi) |
|
زبان مقاله منتشر شده |
en |
موضوعات مقاله منتشر شده |
|
نوع مقاله منتشر شده |
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|