TENSILE AND FRACTURE CHARACTERISTICS OF A SIC- PARTICLE-REINFORCED 7075 ALUMINIUM ALLOY |
|
| چکیده انگلیسی مقاله |
Fracture behavior of a 7075 aluminium alloy reinforced with 15 Vol%. SiC particles was studied after T6 and annealing heat treatments under uniaxial tensile loading at room temperature. The scanning electron microscopy of fractured surfaces and EDS analysis showed:, that fracture mechanism changed from due mainly to fractured particle in T6 condition to interface decohesion in samples in annealed state. Different fracture mechanisms in annealed and T6 conditions can be ascribed mainly to the significant difference in the stress concentration levels around the particles. In T6 condition, very high local stress sufficient to cause fracture of particle can be generated during loading, while the presence of large precipitates at the particle/matrix interface produced interface decohesion leading to final fracture in the annealed state. |
|
| کلیدواژه‌های انگلیسی مقاله |
|
|
| نویسندگان مقاله |
رزاقیان a | razaghian a
imam khomeini international university, qazvin, iran
سازمان اصلی تایید شده: دانشگاه بین المللی امام خمینی (Imam khomeini international university)
yu d | yu d
کاندرا t | chandra t
|
|
| نشانی اینترنتی |
http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1-50&slc_lang=fa&sid=en |
| فایل مقاله |
دریافت فایل مقاله |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
گروه سرامیک |
| نوع مقاله منتشر شده |
Research paper |
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|