عنوان انگلیسی Microstructure and Crystallographic Texture Characterization of Friction Stir Welded Thin AA2024 Aluminum Alloy
چکیده انگلیسی مقاله Friction stir welding (FSW) is a promising technique to join aluminum alloys without having problems encountered during fusion welding processes. In the present work, the evolution of microstructure and texture in friction stir welded thin AA2024 aluminum alloy are examined by electron backscattered diffraction (EBSD) technique. The sheets with 0.8 mm thickness were successfully welded by friction stir welding at the tool rotational speeds of 500, 750, and 1000 rpm with a constant traverse speed of 160 mm/min. EBSD revealed that stir zones exhibited equiaxed recrystallized grains and the grain size increased with increasing the tool rotation rate. The fraction of high angle grain boundaries and mean misorientation angle of the boundaries in the FSW joints at 500 rpm were 63.6% and 24.96°, respectively, which were higher than those of the sample welded at 1000 rpm (53.6% and 17.37°). Crystallographic texture results indicated that the Cube {001}< 100> and S {123}< 634> textures in base metal gradually transformed in to Copper {112}< 111> shear texture. It was found that with increasing the tool rotation rate, the intensity of Cube {001}< 100>, Y {111}< 112>, S {123}< 634>, and Dillamore {4 4 11}< 11 11 8> texture orientations increased and the intensity of Brass {011}< 211> texture orientation decreased. 
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m الوند | m. alvand
faculty of materials and metallurgical engineering, semnan university, semnan, iran

سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

m ناصری | m. naseri
department of materials science and engineering, faculty of engineering, shahid chamran university of ahvaz, ahvaz, iran

سازمان اصلی تایید شده: دانشگاه شهید چمران (Shahid chamran university)

e برهانی | e. borhani
department of nano technology, nano materials group, semnan university, semnan, iran

سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

h عبداله پور | h abdollah pour
faculty of materials and metallurgical engineering, semnan university, semnan, iran

سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1548-2&slc_lang=en&sid=en
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/454/article-454-567425.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مکانیکی و شکل دادن
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات