International Journal of Iron and Steel Society of Iran، جلد ۱۴، شماره ۱، صفحات ۲۳-۳۰
عنوان فارسی Effects of martensite reversion parameters on the formation of nano/ultrafine grain structure in AISI ۳۰۴L stainless steel
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effects of Martensite Reversion Parameters on the Formation of Nano/ultrafine Grain Structure in AISI 304L Stainless Steel
چکیده انگلیسی مقاله Formation of nano/ultrafine grain structure in AISI 304L austenitic stainless steel through the martensite reversion treatment was studied. The solution annealed specimens were cold rolled up to 95 % thickness reduction at -15°C. The cold-rolled specimens were subjected to reversion annealing treatment at the temperature range of 700-1000 °C for 10–150 min. Microstructural evolutions were analyzed using ferritscopy, X-ray diffraction, and field emission scanning electron microscopy techniques, whereas mechanical properties were determined by hardness test. The saturation strain during cold rolling was about 56 % reduction. The mean austenite grain size of 135 nm was obtained by 95 % cold reduction and annealing at 700 °C for 10 min. It was found that increasing cold reduction resulted in grain refinement at the same condition of reversion annealing and higher hardness.
کلیدواژه‌های انگلیسی مقاله Nano/ultrafine, Stainless steel, Cold work, Reversion annealing
نویسندگان مقاله حجت اسفندیاری |
department of materials engineering, isfahan university of technology, isfahan 84156- 83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

سیدرضا حسینی | s r
department of materials engineering, maleke-ashtar university of technology, isfahan 83145-115, iran

f اشرفی زاده |
department of materials engineering, isfahan university of technology, isfahan 84156- 83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

a کرمانپور |
department of materials engineering, isfahan university of technology, isfahan 84156- 83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات