عنوان انگلیسی SURFACE HARDENING OF TUNGSTEN-BASED HEAVY ALLOY VIA PACK BORONIZING
چکیده انگلیسی مقاله The boronizing of a tungsten heavy alloy containing Ni and Fe as the major alloying elements were performed in the present study to increase its surface hardening. Pack cementation method was employed as a well-known, successful solid-state process for boronizing. The coating treatment was accomplished at different temperatures of 1000, 1050 and 1100°C for 6 and 9 hours. The formation of tungsten boride phase was confirmed, although a silicide layer covered the surface of the specimen as the outer layer. The mechanism of the formation of a multilayered surface was explained. The maximum thickness of reaction zone and surface hardness achieved in the current work were 300 µm and 2470 HV, respectively.
کلیدواژه‌های انگلیسی مقاله Tungsten alloy, Hardening, Boronizing, Pack cementation
نویسندگان مقاله a عطایی | a. ataei
tehran


m جلالی | m. jalaly
tehran


m تمیزی فر | m. tamizifar
tehran
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-375-2&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سطح پوشش و خوردگی
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات