عنوان انگلیسی SYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD
چکیده انگلیسی مقاله The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusting pH. The precipitated powders were then calcined to obtain a mixture of their oxides as NiO and NiAl2O4 which were reduced in a carbon bed at various temperatures up to 1300. Proper temperature for calcination in air was determined through TG analysis; 900. SEM observation of powders after reduction, revealed micro-sized Ni particles, along with fin distribution of Ni and Al2O3 elements. XRD analysis of the calcined sample showed the presence of NiAl2O4 and NiO and the same analysis for the reduced sample confirmed the formation of Al2O3 and Ni.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله n مسکنی | n. maskani
narmak, 16844 tehran, iran


r نقی زاده | r. naghizadeh
narmak, 16844 tehran, iran


a میرحبیبی | a. mirhabibi
narmak, 16844 tehran, iran


h رضایی | h. rezaie
narmak, 16844 tehran, iran
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-75-5&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات