عنوان انگلیسی Optimization of Friction Stir Welding Parameters for Dissimilar Joining of Aluminum Alloy 2024 and Magnesium Alloy AZ91C Using Taguchi Method
چکیده انگلیسی مقاله In this research, friction stir welding (FSW), a solid-state joining process, was employed to weld 5 mm thick sheets of aluminum alloy Al2024 and magnesium alloy AZ91C. The Taguchi design of experiments method was utilized to optimize the FSW process parameters including tool rotational speed (800-1600 rpm), welding speed (8-20 mm/min), and plunge depth (0.2-0.4 mm) to achieve maximum hardness in the weld zone. Microstructural characterization was studied using optical and scanning electron microscopes. The optimum parameters were found to have a 1600 rpm rotational speed, 8 mm/min welding speed, and 0.4 mm plunge depth, resulting in a maximum hardness of 148 HV in the stir zone (SZ). The layered or onion ring structure observed in the SZ was attributed to insufficient mixing and elemental diffusion between the dissimilar alloys due to the short interaction time during welding. Scanning electron microscopy revealed the formation of a continuous intermetallic layer at the aluminum-magnesium interface and the dispersion of magnesium particles in the aluminum matrix, contributing to the composite-like structure in certain regions. The hardness variation perpendicular to the weld line was correlated with the microstructural evolution, with the highest hardness observed in the fine-grained SZ due to grain refinement and precipitation hardening. The thermomechanically affected zone (TMAZ) exhibited lower hardness due to the presence of coarser precipitates and partially recrystallized grains. This research demonstrates the feasibility of joining Al2024 and AZ91C alloys using FSW and highlights the importance of optimizing process parameters to achieve desirable mechanical properties and microstructural characteristics in the dissimilar weld joint.
کلیدواژه‌های انگلیسی مقاله Optimization,Friction Stir Welding,Dissimilar joining,taguchi method
نویسندگان مقاله S. Rouhi |
Department of Mechanical Engineering, Faculty of Engineering, Urmia University, Urmia, Iran

A. Doniavi |
Department of Mechanical Engineering, Faculty of Engineering, Urmia University, Urmia, Iran

M. Shahbaz |
Department of Materials Science and Engineering, Faculty of Engineering, Urmia University, Urmia, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_7601_d00e69b381a108ea63c94bfc90c08243.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات