Comparison of Endodontic Medicaments on Bond Strength of Fiber Post to Root Dentin Using Resin Cement |
|
چکیده انگلیسی مقاله |
Statement of the Problem: Endodontic irrigants and medicaments may affect the bond strength of intracanal posts to root dentin. Purpose: The aim of this study was to compare the effect of calcium hydroxide (Ca(OH) 2 ) and 2% chlorhexidine gel (CHX) on bond strength of fiber post cemented with resin cement to root dentin. Materials and Method: This in vitro experimental study was conducted on 36 mandibular premolars. Canals were prepared using the step back technique. After root canal irrigation, the teeth were divided into three groups of 12. Ca(OH) 2 paste and CHX gel were used as intracanal medicaments in the first and second groups respectively. No intracanal medicament was used in the third group (control group). Access cavities were then sealed and the teeth were incubated for one week. The root canals were then filled using gutta percha and AH26 sealer and the teeth were incubated for 72 hours. Tooth crowns were then cut at the level of the cementoenamel junction and intracanal posts were placed. The teeth were mounted in auto-polymerizing acrylic resin, and incubated for one week .They were then sectioned into 1.5mm thick slices from their coronal surface using a fully automated cutting machine, and subjected to push-out test until failure. The load at debonding was recorded and data were analyzed using one-way ANOVA, post-hoc test and t-test. The coronal margin of the root was at the level of the surface of acrylic resin in the mold. Results: The mean bond strength was 4.45 MPa in the Ca(OH) 2 , 2.45 MPa in the CHX and 2.48 MPa in the control group. The difference in this regard was statistically significant among groups ( p = 0.04). The Ca(OH)2 group had significant differences with the CHX and control groups ( p = 0.03 and p = 0.02, respectively). The difference between the CHX and control groups was not significant ( p = 0.974). Conclusion: Based on the results, Ca(OH) 2 increased the bond strength of fiber post to root dentin but 2% CHX had no effect on bond strength. Keywords ● Chlorhexidine ● Calcium Hydroxide ● Fiber Post ● Resin Cement |
|
کلیدواژههای انگلیسی مقاله |
|
|
نویسندگان مقاله |
مریم زارع جهرمی | maryam zare jahromi dept. of endodontics, dental school faculty , isfahan khorasgan branch, islamic azad university, isfahan, iran.
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)
مهرداد برکتین | mehrdad barekatain dept. of operative dentistry, dental school faculty , isfahan khorasgan branch, islamic azad university, isfahan, iran.
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)
شیرین روانبد | shirin ravanbod dentist, shiraz, iran.
پریسا رنجبریان | parisa ranjbarian dept. of endodontics, dental school faculty , shahrekord university of medical sciences, shahrekord, iran.
سارا kousehlar | sara kousehlar post graduate student, dept. of endodontics, dental school faculty , isfahan khorasgan branch, islamic azad university, isfahan, iran.
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)
|
|
نشانی اینترنتی |
http://dentjods.sums.ac.ir/index.php/JDSUMS/article/view/1385 |
فایل مقاله |
اشکال در دسترسی به فایل - ./files/site1/rds_journals/331/article-331-323401.pdf |
کد مقاله (doi) |
|
زبان مقاله منتشر شده |
en |
موضوعات مقاله منتشر شده |
|
نوع مقاله منتشر شده |
Original Article |
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|