عنوان فارسی Preparation and Mechanical Properties of Nano/Ultrafine Bainitic Structure in AISI ۵۲۱۰۰ Steel
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Preparation and Mechanical Properties of Nano/Ultrafine Bainitic Structure in AISI 52100 Steel
چکیده انگلیسی مقاله The development of nano/ultrafine bainitic structure in AISI 52100 steel was the goal of this study. For this purpose,
the AISI 52100 the specimens were austenitized at 1050 °C for 60 min followed by low-temperature austempering
treatment at different temperatures and times. The austempered samples were characterized using field emission
scanning electron microscopy (FESEM), X-ray diffraction (XRD) and tension test. According to achieved results,
the microstructure of AISI 52100 steel after the austempering treatment consisted of ultrafine bainitic ferrite plates
and retained austenite with two morphologies of micrometer-block and fine film. At the austempering temperature
up to 250 °C, the micrometer-blocky morphology of austenite completely vanished from the microstructure, and
the strength and ductility increased to about 2000 MPa and 7 %, respectively. By increasing the austempering
temperature to 300 °C, the strength and ductility reduced (to about 1808 MPa and 3 %) simultaneously as a result
of changing in the shape and size of bainite phase.
کلیدواژه‌های انگلیسی مقاله Nanostructures, 52100 steel, X-ray diffraction, Mechanical Properties
نویسندگان مقاله m طاووسی |
department of material engineering, malek- ashtar university of technology mut , shahin-shahr, isfahan, iran
سازمان اصلی تایید شده: دانشگاه صنعتی مالک اشتر (Malek ashtar university of technology)

m نوربخش |
department of material engineering, malek- ashtar university of technology mut , shahin-shahr, isfahan, iran
سازمان اصلی تایید شده: دانشگاه صنعتی مالک اشتر (Malek ashtar university of technology)

سیدرضا حسینی | s r
department of material engineering, malek- ashtar university of technology mut , shahin-shahr, isfahan, iran
سازمان اصلی تایید شده: دانشگاه صنعتی مالک اشتر (Malek ashtar university of technology)

نشانی اینترنتی http://journal.issiran.com/article_23711_80029ddd3acec9b7c0f3224e548d9910.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/419/article-419-316488.pdf
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات