Iranian Journal of Chemistry and Chemical Engineering، جلد ۴۰، شماره ۲، صفحات ۵۸۱-۵۹۲
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Application of MEA, TEPA and Morpholine Grafted NaY Zeolite as CO2 Capture
چکیده انگلیسی مقاله In the current research, NaY zeolite with a molar ratio of Si/Al=2.5 was grafted chemically with amines like monoethanolamine, tetraethylenepentamine, and morpholine.The modified NaY zeolites were characterized by XRD, FT-IR, TGA, EDAX, BET, FESEM, CO2-TPD, and Volumetric analysis. Modification of the NaY surface with amine groups led to a remarkable rise in CO2   adsorption capacity. CO2 adsorption studies of  NaY and modified NaY zeolite by CO2-TPD technique revealed that, the dominant mechanism involves the interaction of CO2 with amine groups on the surface of NaY zeolite, at ambient pressure and at a temperature of 323 K. The volumetric method was also used to investigate CO2 adsorption onto the amine grafted NaY zeolite at 5, 7 bar pressures and at temperatures of 298 and 343 K. The adsorption process is thermal dependence and results of adsorption studies indicate that increasing temperature leads to higher adsorption of CO2
onto the amine grafted NaY zeolites.
کلیدواژه‌های انگلیسی مقاله CO2-TPD,monoethanolamine,Tetraethylenepentamine,Morpholine,Amine grafted NaY zeolite,CO2 capture,Volumetric method
نویسندگان مقاله Heshmatollah Alinezhad |
Faculty of Chemistry, University of Mazandaran, Babolsar, I.R. IRAN

Mohammadreza Fakhimi Abarghouei |
Faculty of Chemistry, University of Mazandaran, Babolsar, I.R. IRAN

Mahmood Tajbakhsh |
Faculty of Chemistry, University of Mazandaran, Babolsar, I.R. IRAN

Khodabakhsh Niknam |
Faculty of Chemistry, Persian Gulf University, Bushehr, I.R. IRAN

نشانی اینترنتی https://ijcce.ac.ir/article_37861_665d463949c474e2d338fb9e9092d33b.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات