Iranian Journal of Chemistry and Chemical Engineering، جلد ۴۱، شماره ۵، صفحات ۱۵۴۹-۱۵۶۰
عنوان فارسی cccc
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Tuning Structural and Optical Properties of Copper Oxide Nanomaterials by Thermal Heating and Its Effect on Photocatalytic Degradation of Congo Red Dye
چکیده انگلیسی مقاله In this study, Copper oxide (CuO) nanoparticles (NPs) were prepared using the chemical co-precipitation method and treated at different calcination temperatures. The synthesized CuO NPs have been calcinated at 300 °C, 500 °C, and 700 °C. The X-Ray Diffraction (XRD) results exhibited a decrease in the width of the principle diffraction peak with the temperature rise. Crystallite size was determined by Scherrer’s formula, whereas, the Williamson-Hall method presented drastic variation in size indicating the creation of lattice strain with the rise in calcination temperature. Scanning Electron Microscopy (SEM) images showed an increase in grain size and vary from 170 nm – 430 nm. X-ray Energy Dispersive Spectroscopy (EDS) results indicate the formation of CuO NPs and relative Cu contents increased (52.9 to 72.5 Atomic percentage) with temperature. Optical properties are also affected by the calcination temperature and a reduction in bandgap is observed with the increase in temperature. Fourier Transform Infra-Red (FT-IR) spectroscopy spectra of different samples showed identical bonding behavior and no apparent change in bonding was observed. Photo-degradation of Congo Red dye was performed with CuO NPs treated at different temperatures and NPs treated at 500 °C, have shown maximum degradation efficiency in 75 min under visible light.
کلیدواژه‌های انگلیسی مقاله Thermal effects,CuO NPs,Calcination,Bandgap tuning,variant chemical composition,photocatalytic activity
نویسندگان مقاله Sidra Rehman |
Department of Physics, University of Agriculture Faisalabad, 38000, Faisalabad, PAKISTAN

Naveed Akhtar Shad |
Department of Physics, Government College University Faisalabad, Faisalabad, PAKISTAN

Muhammad Munir Sajid |
Henan Key Laboratory of Photovoltaic Materials, School of Physics, Henan Normal University, Xinxiang 453007, P.R. CHINA

Khuram Ali |
epartment of Physics, University of Agriculture Faisalabad, 38000, Faisalabad, PAKISTAN

Yasir Javed |
Department of Physics, University of Agriculture Faisalabad, 38000, Faisalabad, PAKISTAN

Yasir Jamil |
Department of Physics, University of Agriculture Faisalabad, 38000, Faisalabad, PAKISTAN

Muhammad Sajjad |
Department of Physics, University of Agriculture Faisalabad, 38000, Faisalabad, PAKISTAN

Ahmed Nawaz |
Department of Physics, University of Agriculture Faisalabad, 38000, Faisalabad, PAKISTAN

Surender Kumar Sharma |
Department of Physics, Central University of Punjab, Bathinda, INDIA

نشانی اینترنتی https://ijcce.ac.ir/article_245941_2105a2ec93c4b8f48aa367901ff49859.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات