Effect of Mechanical Alloying and Sintering on Phase Transformation, Microstructural Evolution, Mechanical Properties and Density of Zr-Cr Alloy |
|
| چکیده انگلیسی مقاله |
The purpose of present research was production ofZr-based alloy as the nuclear fuel cladding by mechanical alloying (MA) and sintering process. Firstly, Zr and Cr powders were mechanically alloyed to produce the refractory and hard Zr-10 wt% Cr alloy, and then, the powder mixtures were consolidated by press and following sintering at temperature of 800˚C min. The phase evolution, microstructural changes, microhardness, and density of the Zr-10 wt% Cr alloy were studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), microhardness measurement, and the Archimedes method. The results showed that the MA increased the solid solubility of the immiscible powders of Cr and Zr; therefore, the Cr atoms were completely dissolved in the Zr lattice after 24 h of the milling time and the nanostructured Zr(Cr) solid solution was obtained with the high microhardness value of about 491 Hv. Also, the results of the density measurement indicated that the resulted density was close to 98% of the theoretical density. |
|
| کلیدواژه‌های انگلیسی مقاله |
mechanical alloying,microhardness,NanoStructured,Sintering,Solubility |
|
| نویسندگان مقاله |
J. Arasteh |
Department of Materials Science and Engineering, Shahid Bahonar University of Kerman, Kerman, Iran
|
|
| نشانی اینترنتی |
https://www.ije.ir/article_113064_f76124cc5a811e97caa5e35a1381a6a5.pdf |
| فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|