عنوان انگلیسی Preparation of Porous Alumina/Nano-Nickel Composite by Gel Casting and Carbothermic Reduction
چکیده انگلیسی مقاله Gel casting, carbothermic reduction, and sintering were used to make a porous alumina-based body containing nickel nano-particles. Effects of dispersant (Tri polyphosphate sodium) amount on gel viscosity, mechanical activation of raw materials, raw materials mixture composition, and reduction atmosphere on the prepared composites and NiO reduction mechanism were investigated. XRD, SEM, and TG-DTA analyses were used to characterize the resulting products. It was found that 2.5 wt % dispersant is an optimum amount for a gel suspension with 50 V% of solid consisting of alumina, graphite, and nickel oxide. XRD results of reduced and sintered product (at 1200-1500 °C) showed that alumina, nickel, and nickel aluminate spinel are present in the prepared composite. SEM images of the composite showed that nickel nanoparticles and porosities with different dimensions are present in the alumina body. The porosity of the composite made with 12 h ball milled-alumina was 48%, while it was 64 % in the sample made with 20 min ball-milled alumina. The results of TG-DTA analyses showed that the reduction temperature and mechanism are dependent on the raw materials’ ball milling time. Thermal analyses revealed that mechanical activation of raw materials decreases the NiO reduction temperature and increases the metallic Ni production.
کلیدواژه‌های انگلیسی مقاله Alumina,nickel,Composite,gel casting,reduction,porosity
نویسندگان مقاله Z. Hosseini |
Department of Materials Engineering, Hamedan University of Technology, Hamedan, Iran

S. Mollazadeh Beidokhti |
Department of Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran

J. Vahdati Khaki |
Department of Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran

M. Pourabdoli |
Department of Materials Engineering, Hamedan University of Technology, Hamedan, Iran

نشانی اینترنتی https://www.ije.ir/article_140031_6465f7c5c82808d3f3e2fc754187f8a7.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات