عنوان انگلیسی Nanostructured α-Fe2O3: Solvothermal Synthesis, Characterization, and Effect of Synthesis Parameters on Structural Properties
چکیده انگلیسی مقاله α-Fe2O3 is a stable, cheap, and non-toxic metal oxide with many advantages and different fields of application. Many attempts have been devoted to the synthesis of α-Fe2O3 with different crystal structures and morphologies to obtain the desired properties. In this research, nanostructured α-Fe2O3 were synthesized by a facile solvothermal route. The as-obtained samples are characterized by XRD, FESEM, EDS, FTIR, and BET surface area analysis. The results showed that the as-synthesized hematite consists of nanostructures with the morphology of distorted microspheres with an average diameter in the range of 1 to 1.5 µm each composed of self-assembled nanoparticles with an average size in the range of 10 to 30 nm. The results showed that the hematite nanostructures had a specific surface area of 41.86 m2g-1. The influence of temperature and duration of the solvothermal process as well as, calcination on the structural properties of the α-Fe2O3 samples was investigated. The results reveal that the crystallite size of the samples increases with increasing the temperature and duration of solvothermal treatment. Moreover, calcination leads to an increase in the crystallite size of the samples. The α-Fe2O3 nanostructures with a minimum crystallite size of 13.6 nm were synthesized at 150 °C for 4 h while the largest crystallite size of 75.4 nm was obtained at 180 °C and 8 h with subsequent calcination of the sample at 500 °C for 1 h. The results of the present study can be useful to enhance the properties of α-Fe2O3 nanostructures in various fields of application.
کلیدواژه‌های انگلیسی مقاله Hematite (α-Fe2O3),Nanostructures,Solvothermal process,Calcination,Crystallite Size
نویسندگان مقاله S. M. R. Shariatzadeh |
Department of Chemical Engineering, Arak Branch, Islamic Azad University, Arak, Iran

M. Salimi |
Department of Chemical Engineering, Arak Branch, Islamic Azad University, Arak, Iran

H. Fathinejad |
Department of Chemistry, Farahan Branch, Islamic Azad University, Farahan, Iran

A. Hassani Joshaghani |
Department of Chemical Engineering, Arak Branch, Islamic Azad University, Arak, Iran

نشانی اینترنتی https://www.ije.ir/article_145930_2e3dc420623c47256c1d06c6a4dfd75f.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات