Iranian Journal of Materials Forming، جلد ۱۰، شماره ۱، صفحات ۵۳-۶۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The Simulation of Texture of Al0.3CoCrFeNi High Entropy Alloy after Cold Deformation using Visco-Plastic Self-Consistent Model
چکیده انگلیسی مقاله In the present study, a visco-plastic self-consistent model (VPSC) was used to predict the Al0.3CoCrFeNi texture after cold rolling. The alloy under examination was produced via vacuum arc remelting and casting (VAR casting). Then, it was remelted four times to have the best structure homogeneity. However, the produced ingot was then homogenized at 1050°C for 10 h to remove the residual stress and reduce the micro-macro-segregation. This was followed by 75% cold reduction which was employed in seven passes. In order to simulate the Al0.3CoCrFeNi texture via the VPSC model, affine schemes and hardening parameters were used in this model. Moreover, this model was performed by Fortran 77 programming languages, and grain fragmentation and co-rotational effect were used in this code. In this study, a simulation process was used for 300 and 1000 grains. After that, simulation results were compared with experimental textures that were measured by the X-ray diffraction method. The results showed that both experimental and simulated textures have an acceptable compatibility. However, there are differences between the measured and simulated results, which can be attributed to the number of grains of estimated and simulated cases.
کلیدواژه‌های انگلیسی مقاله crystal plasticity, Cold rolling, High entropy alloys, Texture
نویسندگان مقاله A.H. Hosseinifar |
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran

K. Dehghani |
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_7015_39ca8702f56e6d843de660dfb82d9624.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات