عنوان انگلیسی A Comparison of Laser and Mechanical Surface Pretreatment Methods on Shear Bond Strength of Resin Composite to Resin-Modified Glass Ionomer
چکیده انگلیسی مقاله Statement of the Problem: Dentin margins have a higher microleakage than enamel in composite restorations due to weaker bond durability. Clinically, most margins are located apical to cementoenamel junction on the dentin or cementum. Different surface preparation methods may have dissimilar effects on the shear bond strength of resin-modified glass ionomer (RMGI) to composite resin, regarding the layering technique employed in restoration of these cavities. Purpose: This study aimed to investigate the shear bond strength of RMGI to composite resin using different mechanical surface preparation methods. Materials and Method: In this in vitro study, 72 RMGI samples were prepared in six groups (n=12): control, acid etching, air abrasion with aluminum oxide (Al2O3), bur, Er: YAG laser, and Er, Cr: YSGG laser groups. Two samples from each group were randomly examined under a scanning electron microscope (SEM). A bonding layer and composite resin were applied and cured. Then the samples were subjected to 5000-cycles thermocycling procedure. The shear bond strength was then evaluated using a universal testing machine. Finally, the failed surface of the samples was evaluated under a light microscope to examine the failure mode. For the statistical analysis, one-way ANOVA and Games-Howell post hoc test was used to compare quantitative variables and chi-squared test to investigate the relationship between the failure mode and the groups. The significant level was set at 0.05. Results: The results showed significant differences between the mean of the strength variable in the groups (p< .001). The acid-etch and air abrasion groups exhibited significantly the lowest and highest values, respectively. The chi-squared test results also showed a significant relationship between the failure mode in the study groups (p= .008). Conclusion: Acid etching before completing RMGI polymerization could adversely affect shear bond strength. The air abrasion and bur methods are among the best methods to increase the shear bond strength between composite resin and RMGI. Using Er, Cr: YSGG and Er: YAG lasers could increase the bond strength results.
کلیدواژه‌های انگلیسی مقاله Lasers, Glass ionomer cements, Composite Resins, Bond Strength
نویسندگان مقاله Faramarz Zakavi |
Dept. of Operative and Esthetic Dentistry, Dental Faculty, Ahvaz Jundishapur Medical Science University, Ahvaz, Iran.

Sarah Gholizadeh |
Dept. of Operative and Esthetic Dentistry, Dental Faculty, Ahvaz Jundishapur Medical Science University, Ahvaz, Iran.

Sana Dibazar |
Dept. of Operative and Esthetic Dentistry, Dental Faculty, Tabriz University of Medical Science, Tabriz, Iran.

Mehdi Esmaeili |
Dept. of Orthodontics Dentistry, Dental Faculty, Tabriz Azad University of Medical Science, Tabriz, Iran.

نشانی اینترنتی https://dentjods.sums.ac.ir/article_48848_220c366f92c88a58f28a26af47a2a3a3.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات