عنوان انگلیسی Effect of different catalyst ratios on the ring-opening metathesis polymerization (ROMP) of dicyclopentadiene
چکیده انگلیسی مقاله In this paper, the polymerization process of polydicyclopentadiene (PDCPD) obtained by using dicyclopentadiene (DCPD) and the 2nd generation Grubbs’ catalyst is optimized. The curing reaction kinetics was studied by differential scanning calorimetry (DSC), and the solidification reaction process was obtained. The effects of different ratios of monomer to catalyst on the product performance were investigated. In addition, the current common modification methods of PDCPD have been summarized and improved. The results showed that with the increase of the ratio of monomer to the catalyst, the tensile strength, tensile modulus, bending strength and bending modulus of PDCPD all showed a downward trend, and the impact strength showed an upward trend. When nDCPD: nCat =10000:1, the comprehensive mechanical properties of PDCPD reached the best. The bending modulus, tensile strength and impact strength of PDCPD achieved 2100 MPa, 52.4 MPa and 30 kJ/m2, respectively. The glass transition temperature (Tg) of PDCPD also showed a decreasing trend with the increase of the ratio of monomer to the catalyst, at this ratio, the Tg of the polymer reached 147.6°C. The catalyst concentration had a large effect on the product performance.
کلیدواژه‌های انگلیسی مقاله polydicyclopentadiene, Kinetics(polym.), Catalyst concentration, reaction injection moulding, ROMP
نویسندگان مقاله Zehan Zhang |
Shanghai Key Laboratory of Multiphase Material Chemical Engineering, East China University of Science and Technology, Shanghai 200237, China

Zaixing Yang |
Sinopec Shanghai Petrochemical Co., Ltd

Fei Zhou |
Sinopec Shanghai Petrochemical Co., Ltd

Xuelian He |
Shanghai Key Laboratory of Multiphase Material Chemical Engineering, East China University of Science and Technology, Shanghai 200237, China

نشانی اینترنتی http://poj.ippi.ac.ir/article_1887_db08993cce50c6cda4189cd83ae0113a.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات