عنوان انگلیسی Effect of replacing EPDM with high molecular weight amorphous poly(1-hexene) on the mechanical behavior of iPP/iPP-g-MA/EPDM blends
چکیده انگلیسی مقاله Varying amounts of a high molecular weight poly(1-hexene) (PH, Mv=1.7×106 Da) are substituted for EPDM in an iPP/iPP-g-MA/EPDM blend (weight ratio: 76:4:20) and mechanical properties as well as phase morphology of the blends are studied and compared. The results show that by substituting the entire EPDM with PH, the tensile strength-at-break increases from 18.7 to 21.1 MPa, elongation-at-break increases from 15.5% to 370.8%, and impact strength increases from 6.4 to 50.1 kJ.m-2. Dynamic mechanical thermal analysis (DMTA) of the blends proved their immiscibility and SEM analysis confirmed these findings by showing droplet-matrix morphologies. Studying the creep behavior of the samples shows that the blends containing PH have more creep so that by substituting all EPDM in the blends with PH, the permanent deformation increases from 0.425% to 0.505%. According to the results, PH is introduced as a candidate for improving the impact properties of iPP/iPP-g-MA/EPDM blend.
کلیدواژه‌های انگلیسی مقاله Rubber toughened iPP, Creep behavior, Two phase morphology, DMTA, Immiscible blends
نویسندگان مقاله Mahsa Mobini-Dehkordi |
Department of Polymer Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran, P.O.Box:71993-3

Gholam-Reza Nejabat |
Department of Applied Researches, Chemical, Petroleum & Polymer Engineering Research Center, Shiraz Branch, Islamic Azad University, Shiraz, Iran

Mohammad-Mahdi Mortazavi |
Faculty of Engineering, Iran Polymer and Petrochemical Institute, Tehran, Iran, P.O. Box: 14975-112

نشانی اینترنتی http://poj.ippi.ac.ir/article_1900_89d8cad68c039774c4fb664cea27ea17.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات