عنوان انگلیسی Influence of Sintering Temperature on the Marginal Fit and Compressive Strength of Monolithic Zirconia Crowns
چکیده انگلیسی مقاله Statement of the Problem: Increasing the sintering temperature is suggested by some manufacturers as a way to enhance the translucency of monolithic zirconia crowns. Meanwhile, its effect on the marginal fit and compressive strength of the restoration is not fully understood. Purpose: This study aimed to evaluate the effect of sintering temperature on the marginal fit and compressive strength of monolithic zirconia crowns.Materials and Method: In this in vitro study, thirty crowns of pre-sintered monolithic zirconia were milled and sintered in a special furnace at either 1450°C or 1550°C (n=15 per group). The marginal gaps were measured at 18 spots on the dies with a digital microscope. To evaluate the compressive strength, the specimens were cemented on brass dies by using conventional glass ionomer cement. Vertical load was applied by a universal testing machine until fracture. One-way ANOVA test was used to analyze the results (α=0.05).Results: The marginal gap was not significantly different between the two groups (p= 0.062). A significantly higher mean value of compressive strength was observed in crowns sintered at 1550°c (1988.27±635.09 N) than those sintered at 1450 °c (1514.27±455.11 N) (p= 0.026).Conclusion: Although increasing the sintering temperature would not affect the marginal gap of monolithic zirconia crowns, it could significantly improve the compressive strength of zirconia restorations.
کلیدواژه‌های انگلیسی مقاله Compressive strength, experimental study, marginal fit, monolithic zirconia, sintering temperature
نویسندگان مقاله Mina Mohghegh |
Dept. of Prosthodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

Sajjad Baseri |
Postgraduate Student, Dept. of Prosthodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

Mohamad Hassan Kalantari |
Dept. of Prosthodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

Rashin Giti |
Dept. of Prosthodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

Seyed Ahmad Ghoraishian |
Dept. of Prosthodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

نشانی اینترنتی https://dentjods.sums.ac.ir/article_48409_aa8856fc0d06c9f4dd48dda477fabe81.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات