عنوان انگلیسی Investigation of Tribological Behavior on the Mechanical Properties of TiB2, Al2O3 Reinforced AA6061 Matrix Sintered Hybrid Composites
چکیده انگلیسی مقاله Hybrid composites consisting of AA6061 matrix reinforced with TiB2 (2, 4, 6, and 8 wt. %), Al2O3 (2 wt. %) particles were produced by the sintering process. In comparison to the base material AA6061, the composite produced had improved mechanical properties. The sintered composites' mechanical properties, such as tensile strength and hardness, are measured and compared to the wear-tested specimen. Optical micrographs reveal that composites were riddled with defects like blowholes, pinholes, and improper bonding between the particulates before sintering. However, the post-sintered optical micrograph showed that the defects were greatly suppressed. Micrographic images revealed the changes in surface characteristics before and after wear. Until a sliding distance of 260 m, the wear rate of the hybrid composites was kept lower than that of the base material. The coefficient of all the composite materials produced for this study was noted to be less than that of the base material. The results reveal that the hardness of hybrid composites having 4 wt. % and 6 wt. % of TiB2 particulates increased by 5.98 % and 1.35 %. Because of the frictional heating during the wear test, the tensile properties lowered by up to 49.6%. It is concluded that the hybrid composites having 4 wt. % and 6 wt. % of TiB2 particulates exhibited less wear rate for extended sliding distance, good hardness, moderate tensile strength, and decent elongation percentage compared to its counterparts.
کلیدواژه‌های انگلیسی مقاله Hybrid composites,sintering,tensile strength,micro hardness,wear,coefficient of friction.
نویسندگان مقاله | Dillibabu Surrya Prakash
VEL TECH RANGARAJAN Dr.SAGUNTHALA R&D INSTITUTE OF SCIENCE AND TECHNOLOGY


| Narayana Dilip Raja
Vel Tech Rangarajan Dr. Sagunthala R&D Institute of Science and Technology
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3670-1&slc_lang=en&sid=1
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مکانیکی و شکل دادن
نوع مقاله منتشر شده Research Paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات