عنوان انگلیسی Morphological and Crystallographic Characterization of Nanoparticles by Granulometry Image Analysis and Rietveld Refinement Methods
چکیده انگلیسی مقاله The particle size distribution of the resultant cobalt ferrite samples was determined from Scanning Electron Microscopy (SEM) images using the granulometry image analysis method. Results showed the nanosized particles of the samples. The X-Ray Diffraction (XRD) patterns of samples were also analyzed by Rietveld refinement method. The results indicated that the precipitated sample at 95 oC had cubic cobalt ferrite structure with F3dm:3 space group and high crystallinity. The lattice parameters, microstrain and crystallite size of samples were also calculated from the XRD pattern. With increasing the precipitation temperature, the crystallite and particle sizes were increased while the lattice parameter and microstrain were decreased. Regarding the results, it can be concluded that the lattice parameter of cobalt ferrite has a diverse relationship with crystallite size.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله Yadolah Ganjkhanlou |
Department of Physical Chemistry, Faculty of Chemical Technology, University of Pardubice, ‎Studentská 573, CZ-532 10 Pardubice, CZECH Republic

Abdolmajid Bayandori Moghaddam |
School of Engineering Science, College of Engineering, University of Tehran, P.O. Box 11155-4563 Tehran, I.R. IRAN

نشانی اینترنتی http://www.ijcce.ac.ir/article_31172_95f8d2447d1f5b4975475e2d1944b2a9.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/444/article-444-2063204.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات