International Journal of Engineering، جلد ۲۵، شماره ۲، صفحات ۱۵۹-۱۶۴
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی PHASE STABILITY AND CONDUCTIVITY OF δ-Bi2O3 WITH MIXTURE OF YTTRIUM AND YTTERBIUM OXIDES
چکیده انگلیسی مقاله In this research Bi2O3 was doped with mixtures of 8, 10, 12 and 18 mol % of Y2O3 and Yb2O3 to stabilizing the δ-Bi2O3 phase using solid state reaction technique. Experimental samples were fabricated by isostatic pressing and sintering at 850 °C for 24 h. X-ray diffraction analysis detected cubic phase (δ-Bi2O3) as the sole stable crystalline phase in samples including 12 and 18 mol % of Y2O3 and Yb2O3. The tetragonal phase was also observed in samples with 8 and 10% mol additives. X-ray diffraction analyses on aged samples at 600 oC with 12 mol % additives revealed that the δ-Bi2O3 phase was transformed to the tetragonal polymorph form. Results of ionic conductivity measurements showed that samples with 12 mol % additives (88 mol % Bi2O3, 8 mol % Y2O3 and 4 mol % Yb2O3) had a higher ionic conductivity than the other samples. 
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله Kamran Ahmadi |


Amir Maghsoudipour |


Masoud Alizadeh |
Ceramic, Material and Energy Research Center(MERC)

نشانی اینترنتی http://www.ije.ir/article_71995_65a08178fafde2f165c3b2c0aa5c5773.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2063045.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات