International Journal of Engineering، جلد ۲۶، شماره ۷، صفحات ۷۰۷-۷۱۲
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Titanium Oxide (TiO2) Coatings on NiTi Shape Memory Substrate Using Electrophoretic Deposition Process
چکیده انگلیسی مقاله The aim of the present research is to convert bioinert surface of NiTi to bioactive and biocompatible surface. In order to develop a bioactive and corrosion resistant film on NiTi, electrophoretic deposition process was done and TiO2 particles were deposited on the NiTi surface. Suspensions including TiO2 particles were prepared using a mixture of acetone and n-butanol (0%, 30%, 60%, 80% and 100% acetone) without using any dispersant. Sedimentation test was used to characterize the suspensions. SEM investigations on surface morphology of coatings shows depositing within 0% acetone cause to crack-free and dense coating with relatively coarse grains and high corrosion resistance.
کلیدواژه‌های انگلیسی مقاله Suspension, TiO2, NiTi, Electrophoretic deposition
نویسندگان مقاله Hossein Maleki-Ghaleh |
Research Center for Advanced Materials and Mineral, Sahand University of Technology

Jafar Khalil-Allafi |
Research Center for Advanced Materials and Mineral, Sahand University of Technology

Vida Khalili |
Department of material, Sahand University of Technology

نشانی اینترنتی http://www.ije.ir/article_72142_d2822b0b3dfa84ac74e1334d15bfd0e3.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2062887.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات