Leaching Kinetics of Stibnite in Sodium Hydroxide |
|
| چکیده انگلیسی مقاله |
Spherical pellets of antimony sulphide were dissolved in 1 molar sodium hydroxide solutions at different temperatures. It was found that the shrinking core with ash layer model could satisfactorily explain the dissolution process. Using this model it was found that initially the rate controlling step is a chemical reaction with activation energy of 10.2 kJ/mol. As the ash layer builds up, diffusion through the ash layer becomes the rate controlling step. The activation energy for this process is 33.4 kJ/mol. |
|
| کلیدواژه‌های انگلیسی مقاله |
|
|
| نویسندگان مقاله |
Mohammad Reza Bakhshandeh |
Materials Science and Engineering, Sharif University of Technology
Manoochehr Hakim |
Materials Science and Engineering, Sharif University of Technology
Mohammad Halali |
Materials Science and Engineering, Sharif Univ. of Technology
Ali Dodangeh |
Materials Sience and Engineering, Sharif University of Technology
|
|
| نشانی اینترنتی |
http://www.ije.ir/article_72258_2d71be114b46bdec9044ad8ad3e97a1f.pdf |
| فایل مقاله |
اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2062789.pdf |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|