عنوان انگلیسی Preparation and Characterization of an Antifouling Polyethersulfone Nanofiltration Membrane Blended with Graphene Oxide/Ag Nanoparticles
چکیده انگلیسی مقاله Graphene oxide/Ag nanoparticles (Ag/GO) was prepared and employed to synthesize antifouling polyethersulfone (PES) mixed matrix membranes. The performance of the membranes was evaluated in terms of flux, hydrophilicity and anti-biofouling properties. With increment of the Ag/GO from 0 to 0.1 wt.%, the pure water flux increased from 24.7 up to 54.1 kg/m2 h. The flux recovery ratio (FRR) of the membranes was performed using milk powder solution and the results illustrated that the 0.1 wt.% Ag/GO membrane had the best fouling resistance with the FRR value of 95.45%. The performance of the nanofiltration was assessed using the retention of Direct Red 16. It was indicated that the Ag/GO-PES membranes have remarkable dye removal (98.38% rejection). The anti-biofouling activities of the 0.1 wt.% Ag/GO mixed matrix membrane was also investigated using activated sludge and the results showed a notable improvement.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله S. Zinadini |


F. Gholami |


E. Noori |


E. Rafiee |


A. A. L. Zinatizadeh |
Applied Chemistry, Razi University

نشانی اینترنتی http://www.ije.ir/article_73023_80b927e3cc77727b5ff5198aeb49e6f6.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2061990.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات