International Journal of Engineering، جلد ۳۱، شماره ۱۰، صفحات ۱۷۷۳-۱۷۸۱
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Probability Approach for Prediction of Pitting Corrosion Fatigue Life of Custom 450 Steel
چکیده انگلیسی مقاله In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress amplitude and elapsed time, t. Fatigue crack growth rates were determined in the near threshold stress intensity factors regime (∆kth). A model was presented for estimation of corrosion fatigue life based on the time to reach critical pit depth (as crack initiation) and crack propagation life. Then. S-N curves were obtained both in air and NaCl solution from axial fatigue testing. Comparison of data from the proposed model and the experimental results (S-N curves) showed good agreement.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله A. Salarvand |
Department of Mechanical Engineering, Islamic Azad University, Doroud Branch, Iran

E. Poursaiedi |
Department of Mechanical Engineering, University of Zanjan, Zanjan, Iran

A. Azizpour |
Department of Mechanical Engineering, University of Zanjan, Zanjan, Iran

نشانی اینترنتی http://www.ije.ir/article_82220_e15c939b429a7cfa2b5f7115a901e833.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2061744.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات