عنوان انگلیسی Air Plasma Sprayed Bond Coat Oxidation Behavior and its Resistance to Isothermal and Thermal Shock Loading
چکیده انگلیسی مقاله An experimental investigation was conducted to find the effect of spraying method of coating of Thermal Barrier Coatings (TBCs) on their oxidation behaviour and resistance to various thermal loading. Isothermal and thermal shock tests were performed in order to study oxidation behaviour of air plasma sprayed Bond Coat (BC) and assess its effect on TBCs lifetime under the stated loadings. Specimens, after loading were investigated using Field Emission Scanning Electron Microscopy (FE-SEM). Results showed in spite of forming various oxide layers within the BC its oxidation in Bond Coat/Top Coat interface behave the same as samples coated by other methods and no failure was observed at substrate/BC interface or within the BC.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله E. Poursaeidi |
Mechanical Engineering Department, Faculty of Engineering, University of Zanjan, Zanjan, Iran

K. Torkashvand |
Mechanical Engineering Department, Faculty of Engineering, University of Zanjan, Zanjan, Iran

M. Mohammadi |
Mechanical Engineering Department, Faculty of Engineering, University of Zanjan, Zanjan, Iran

نشانی اینترنتی http://www.ije.ir/article_89320_c9a63fa34993e2dd90aefac600cd8d23.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2061581.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات