عنوان انگلیسی Effect of Preheating and Precooling on the Flexural Strength and Modulus of Elasticity of Nanohybrid and Silorane-based Composite
چکیده انگلیسی مقاله Statement of the Problem: Composite resin may be used in different temperatures; it is crucial to determine the effect of temperature on mechanical properties of nanohybrid and silorane-based composite.Purpose: This in vitro study compared the flexural strength and modulus of elasticity of nanohybrid and silorane-based resin composite, at 4˚C, room temperature (25˚C), and 45˚C.Materials and Method: In this experimental study, 60 specimens were prepared in a metal split mold (2×2×25mm). Two different resin composites, Filtek Z250 XT (3M/ ESPE) and Filtek P90 (3M/ESPE), were evaluated. The material were inserted into split molds at room temperature, 4˚C or 45˚C and cured with LED (1200 mW/cm2) for 20 seconds in four points (n=10). Then, a three-point bending test was performed using a universal testing machine at a crosshead speed of 0.5 mm/min for measuring the flexural strength and flexural modulus of samples. The data were analyzed by the two-way ANOVA and Tukey test (p< 0.05).Results: The mean highest flexural strength was observed at 45˚C, showing statistically significant difference with flexural strength at 4˚C (p= 0.0001) and 25˚C (p= 0.003) regardless of the type of resin composite. The flexural modulus at 45˚C was highest, showing the statistically significant difference with flexural modulus at 4˚C (p= 0.0001) and 25˚C (p= 0.002). The flexural modulus was statistically different between nanohybrid and silorane-based resin composite (p= 0.01) in 25˚C and 45˚C, but there were no statistically significant differences between flexural strength of Filtek Z250 XT and Filtek P90 regardless of the temperatures (p= 0.062).Conclusion: Preheating the resin composite at 45˚C improves flexural strength and modulus of nanohybrid and silorane-based resin composite. However, flexural strength and modulus of the tested materials were not affected by precooling. The flexural modulus of nanohybrid resin composite was significantly higher than silorane-based resin composite in 25˚C and 45˚C temperatures.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله Farahnaz Sharafeddin |
Biomaterial Research Center, Dept. of Operative Dentistry, School of Dentistry, Shiraz University of Medical Science, Shiraz, Iran.

Mehran Motamedi |
Dept. of Operative Dentistry, School of Dentistry, Shiraz University of Medical Science, Shiraz, Iran.

Zahra Fattah |
Post Graduate Student, Student Research Committee, Dept. of Operative Dentistry, School of Dentistry, Shiraz University of Medical Science, Shiraz, Iran.

نشانی اینترنتی http://dentjods.sums.ac.ir/article_43542_0a11322fcd616067284061214008b3c3.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/331/article-331-1570669.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات