Polyolefins Journal، جلد ۱، شماره ۲، صفحات ۱۱۷-۱۲۹
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The role of 1-hexene comonomer content in thermal behavior of medium density polyethylene (MDPE) synthesized using Phillips catalyst
چکیده انگلیسی مقاله In this work, the role of comonomer content of 1-hexene-medium density polyethylene (MDPE) copolymer,synthesized using Phillips catalyst, on thermal behavior parameters such as: crystallization, melting temperatureand thermal degradation was investigated in detail. The copolymer was fractionated to homogenous short-chainbranching (SCB) fractions by "preparative temperature rising elution fractionation" (P-TREF) method and then itwas subjected to thermal analyses. A broad chemical composition distribution (CCD) in terms of SCB content andmolecular weight (Mw) was observed by P-TREF and gel permeation chromatography (GPC), respectively. Basedon P-TREF results, a parabolic relationship between methylene sequence length (MSL) and elution temperature(ET) was presented. Differential scanning calorimetry (DSC) showed distinct, well-defined melting peaks over a22 °C temperature range for SCB contents of about 3-12 (br/1000 C). The variations in physical characteristicssuch as melting temperature (Tm), crystallinity (Xc), crystallization temperature (Tc) and lamellae thickness (Lc)against SCB content were correlated. Thermogravimetric analysis (TGA) suggested linear relationships betweenthe temperature at maximum degradation rate (Tmax) as well as the degradation initiation temperature (T5%) versusSCB content. Moreover, the TGA curves exhibited distinct differences at both initiation and propagation stages ofthermal degradation at dissimilar comonomer contents.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله عباس کبریت چی |
iran polymer and petrochemical institute, 14965-115, tehran, iran|leibniz-institut für polymerforschung dresden e.v., d-01069, dresden, germany

مهدی نکومنش |
iran polymer and petrochemical institute, 14965-115, tehran, iran

فریدون محمدی |
iran polymer and petrochemical institute, 14965-115, tehran, iran

حسینعلی خنکدار | hossein ali
iran polymer and petrochemical institute, 14965-115, tehran, iran|leibniz-institut für polymerforschung dresden e.v., d-01069, dresden, germany

نشانی اینترنتی http://poj.ippi.ac.ir/article_1099_338.html
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات