عنوان انگلیسی Effect OF SI and AL on the Microstructure, Mechanical Properties and Machinability of 65CU-35ZN Brass
چکیده انگلیسی مقاله Relations between the microstructure, mechanical properties and machinability of as-cast 65Cu-35Zn brass with various amounts of Al from 0 to 4.72 and Si from 0 to 3.62 wt% were investigated. Both Si and Al initially enhanced the UTS and toughness of the brass samples, which led to improvement in machinability due to a reduction in the main cutting force. A duplex brass with random oriented α plates in β' matrix was found to have the best machinability among the other microstructures. It was found that beside the presence of brittle phases, such as β' phase in the microstructure, the morphology and hardness of the phases involved had significant influence on machinability.
کلیدواژه‌های انگلیسی مقاله Brass, Silicon, Aluminum, microstructure, machinability
نویسندگان مقاله | M. Adineh
Shahid Bahonar University of Kerman


| H. Doostmohammadi
Shahid Bahonar University of Kerman


| R. Raiszadeh
Shahid Bahonar University of Kerman
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1677-1&slc_lang=en&sid=1
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/454/article-454-1398283.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات