عنوان انگلیسی Ibuprofen-Loaded CTS/nHA/nBG Scaffolds for the Applications of Hard Tissue Engineering
چکیده انگلیسی مقاله Background: This study addressed the development of biodegradable and biocompatible scaffolds with enhanced biomechanical characteristics. The biocompatibility and the cationic nature of chitosan (CTS) make it more effective as a bone grafting material. Methods: The hydroxyapatite nanoparticles (nHA) were synthesized by hydrothermal method, and bioglass (nBG) (50% SiO2-45% CaO-5% P2O5) was synthesized using sol-gel method. The ibuprofen-loaded CTS/nHA and CTS/nBG scaffolds were fabricated by using freeze-drying method. Results: Transmission electron microscopy image of nHA and nBG revealed the particles of less than 200 nm. The scanning electron microscopy (SEM) images of CTS/nHA and CTS/nBG scaffolds showed pore sizes ranging from 84-190 µm. The physiochemical characteristics of synthesized ceramic nanoparticles and scaffolds analyzed by XRD were confirmed by ICDD 9-432. The porosity of scaffolds was measured by using SEM, Brunauer-Emmett-Teller method and Archimedes' principle. The open porosities of CTS/nBG and CTS/nHA samples were 29% and 31%, respectively. The compressive strength of scaffolds was evaluated by stress vs. strain curve. The CTS/nHA scaffold revealed 4% more water retention capacity than CTS/nBG scaffold. In the presence of lysozyme, CTS/nBG scaffold degraded 32.8%, while CTS/nHA degraded 26.1% in PBS solution at pH 7.4. The density of all scaffolds was found (1.9824 g/cm-3 and 1.9338 g/cm-3) to be nearly similar to that of the dry bone (0.8-1.2 g/cm-3). Fibroblast cells multiplied two times in the sample medium of CTS/nBG after 14 days. After 72 h, CTS/nBG and CTS/nHA scaffolds demonstrated 52% and 46% drug release, respectively. Conclusion: Based on our findings, ibuprofen-loaded scaffolds could be an effective drug delivery system for tissue engineering applications.
کلیدواژه‌های انگلیسی مقاله Chitosan, Fibroblast, Ibuprofen, Nanoparticles
نویسندگان مقاله | Pawan Kumar
Department of Materials Science and Nanotechnology, Deenbandhu Chhotu Ram University of Science and Technology, Haryana, India


| Brijnandan S. Dehiya
Department of Materials Science and Nanotechnology, Deenbandhu Chhotu Ram University of Science and Technology, Haryana, India


| Anil Sindhu
Department of Materials Science and Nanotechnology, Deenbandhu Chhotu Ram University of Science and Technology, Haryana, India
نشانی اینترنتی http://ibj.pasteur.ac.ir/browse.php?a_code=A-10-1-752&slc_lang=en&sid=1
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/125/article-125-1398131.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده Tissue Engineering and Cell Biology
نوع مقاله منتشر شده مقاله کامل
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات