عنوان انگلیسی Effect of Light Intensity and Flowable Liner on Microleakage of Class V Composite Resin Restorations
چکیده انگلیسی مقاله Statement of problem: Polymerization shrinkage stress is the most important causal factor in the microleakage of composite restorations. Relief of this stress with application of low intensity light and low elasticity liner may lead to a decrease in microleakage. Purpose: The aim of this study was to evaluate the effect of light intensity and flowable composite on the microleakage of class V microhybrid composite restorations. Materials and method: In this experimental study, 56 intact bovine incisior teeth were selected. Standard class V cavities were prepared in buccal surfaces and the teeth were randomly divided into 4 groups of 14. All teeth were restored with Tetric ceram and Excite was used as bonding system: Group 1: conventional cure with 40 seconds 550 mW/cm2 light intensity. Group 2: soft- start (s.s) cure with initial intensity (10 seconds 150 mW/cm2) and then final intensity (30 seconds 550 mW/cm2). In groups 3 and 4: the same curing methods were as groups 1 and 2 perfomed, but flowable composite (Tetric flow) was used as liner. After 24 hours water storage samples were, thermocycled, and were immersed in 2% methylene blue for 24 hours. Dye penetration was evaluated using stereomicroscope. The statistic analyses were performed by Kruskal-Wallis and Mann-Whitney tests Results: In general, the gingival margins had significantly more microleakage than the incisal margins (p< 0.05). Microleakage at gingival margin significantly increased with application of flowable liner and soft-start curing (p< 0.05). Conclusion: The result of this study indicated that soft start curing and flowable liner significantly increase microleakage at the gingival margin.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله f شفیعی | f shafiei
assistant professor, department of operative dentistry, school of dentistry, shiraz university of medical sciences, shiraz, iran

سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)

دکتر مهتاب | m memarpour
assistant professor, department of pediatric dentistry, school of dentistry, shiraz university of medical sciences, shiraz, iran

سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)

نشانی اینترنتی http://dentjods.sums.ac.ir/index.php/JDSUMS/article/view/351
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات