عنوان انگلیسی PLASTIC DEFORMATION BEHAVIOUR AT THE WORN SURFACE OF NOVEL CAST AL-ALLOY-TICP COMPOSITE
چکیده انگلیسی مقاله An AI-7wt%Si-5vol%TiCp was worn against a cast iron disc in a tri-pin-on-disc machine, under dry sliding conditions at the sliding speed of 0.24 m/s and applied loads of 6, 20 and 40 N/pin. Stress-strain (`3-^9) curves were constructed by measuring the microhardness and the equivalent strain gradients in near surface regions on the cross-sectional surface prepared parallel to sliding direction.It was shown that, both the magnitude of plastic strains and the depth of plastic deformed zones increased with the applied load. The material exhibited considerable work softening in addition to work hardening at the highest applied load. The softened layer placed just beneath the mechanical mixed layer (MML), was mostly covered with the fine fractured eutectic Si and TiC fragments most of which were associated with microcracks at Al/Si and Al/TiC interfaces. The results were discussed in terms of some of the current work hardening models.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله ثقفیان لاریجانی h | saghafian larijani h


rainforth w m | rainforth w m


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1-15&slc_lang=fa&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات