عنوان انگلیسی SYNTHESIS OF ULTRA-FINE PARTICLES OF BAFE12O19 BY CO- PRECIPITATION ROUTE USING CHLORIDE/NITRATE PRECURSORS
چکیده انگلیسی مقاله Ultra-fine particles of barium hexaferrite have been synthesized by co-precipitation method using barium nitride and iron chloride precursors with a Fe/Ba molar ratio of 11. Co-precipitation was carried out at 25 and 80°C using NaOH as a precipitant. Effect of coprecipitation and annealing temperatures on the phase composition and morphology of the products have been investigated using XRD and SEM, respectively. XRD results indicated existence of BaFeO3-x as a major phase in co-precipitated samples. Analysis of the XRD results also revealed that barium hexaferrite starts to form at a relatively low temperature of 700°C for sample synthesized at 80°C. SEM micrographs exhibit plate-like hexagonal particles of barium hexaferrite for calcined samples. The SEM results showed that the mean particle size of co-precipitated sample at 25°C is smaller than that of 80°C after calcining.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله شیخی مقدم k | sheikhi moghaddam k
department of materials science engineering, faculty of engineering, tehran university, tehran, iran

سازمان اصلی تایید شده: دانشگاه تهران (Tehran university)

عطایی a | ataie a
department of materials science engineering, faculty of engineering, tehran university, tehran, iran

سازمان اصلی تایید شده: دانشگاه تهران (Tehran university)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1-64&slc_lang=fa&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات