عنوان انگلیسی THEORETICAL AND EXPERIMENTAL EVALUATION OF DISLOCATION DENSITY IN A WORKPIECE AFTER FORMING
چکیده انگلیسی مقاله Abstract: The theoretical calculation of dislocation density in different regions of a deformed workpiece of 99.99% pure copper has been carried out using different procedures consisting of Finite Element Method (FEM) and hardness measurement. To assess the validity of the results pertaining to these procedures, the dislocation density is experimentally measured utilizing the Differential Scanning Calorimetry (DSC). Comparing the predicted and experimental results, it was found that the average error in prediction of the dislocation density by the hardness measurement and FEM is 12% and 2.5%, respectively. Also, for further confirmation of the evaluated dislocation density of each region of the deformed workpiece, the annealing process was carried out and in the region of higher dislocation density, a finer grain size was observed.
کلیدواژه‌های انگلیسی مقاله Keywords, Dislocation density, FEM, DSC, Hardness.
نویسندگان مقاله a کریمی طاهری | a karimi taheri


کاظمی نژاد | kazeminezhad


a kiet tieu | a kiet tieu


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-1&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات