Iranian Journal of Materials Science and Engineering، جلد ۵، شماره ۲، صفحات ۲۲-۳۱
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی CHARACTERIZATION OF TRANSVERSE CRACK AND CRACK GROWTH IN A RAILWAY RAIL
چکیده انگلیسی مقاله Abstract: To ensure the rail transportations safety, evaluation of fatigue behavior of the rail steel is necessary. High cycle fatigue behaviour of a rail steel was the subject of investigation in this research using fracture mechanics. Finite element method (FEM) was used for analyzing the distribution of the stresses on the rail, exerted by the external load. FEM analysis showed that the maximum longitudinal stresses occurred on the railhead. To find out about the relation of crack growth with its critical size, and to estimate its lifetime, the behaviour of transverse cracks to rail direction was studied using damage tolerance concept. It revealed that transverse crack growth initially occurred slowly, but it accelerated once the crack size became larger. Residual service life was calculated for defective segments of the rails. In addition, allowable crack size for different non-destructive testing intervals was determined the allowable crack size decreased as the NDT intervals increased.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله علیرضا حسنی | a hassani
department of materials science and engineering, faculty of engineering, semnan university, semnan,iran

سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

r روایی | r ravaee


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-25&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات