عنوان انگلیسی THE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
چکیده انگلیسی مقاله Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing the aluminum amount to %8, only Al oxide formed due to decreasing carbon potential of thealloy,homogenity of elemental concentration in matrix and no diffusion of oxygen through oxide–metalinterface,therefore it has superior oxidation resistance. Meanwhile,oxidation tests showed that the weight gain of thesteel at high temperature oxidation even at 1300ºC was too low.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m عضو امینیان | m ozve aminian
school of metallurgy and materials engineering, iran university of science and technology, tehran, iran

سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

j حجازی | j hedjazi


y خرازی | y kharazi


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-99&slc_lang=en&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات