عنوان انگلیسی MECHANISMS OFPRECIPITATES FORMATION IN AN Al- Cu- Li-ZrALLOYUSINGDSC TECHNIQUE AND ELECTRICALRESISTANCE MEASUREMENTS
چکیده انگلیسی مقاله Abstract: Guinier-Preston (GP) zone formation and precipitation behavior of T1 (Al2CuLi) phase during the ageingof an Al-Cu-Li-Zr alloy was studied by differential scanning calorimetry (DSC) technique and electrical resistancemeasurement of the samples. Results show that endothermic effects in the thermograms of the alloy between 180°Cand 240°C can be related to the enthalpy of GPzones dissolution. Formation of GPzones in the structure increasedhardness, tensile strength and electrical resistance of the Al-Cu-Li-Zr alloy. Furthermore, precipitation of T1 phaseoccurred in temperature range of 250ºC to 300ºC whereas its dissolution occurred within the temperature of 450-530ºC. Activation energies for precipitation and dissolution of T1 phase which were determined for the first time inthis research, were 122.1(kJ/mol) and 130.3(kJ/mol) respectively. Results of electrical resistance measurementsshowed that an increase in the aging time resulted in the reduction of electrical resistance of the aged samples.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a شکوه فر | a shokuhfar
department of material science, faculty of mechanical engineering, k. n. toosi university of technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی خواجه نصیرالدین طوسی (Khajeh nasir toosi university of technology)

احمدی | s ahmadi
department of material science, faculty of engineering, tarbiat modares university, tehran, iran.

سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

h عربی | h arabi
centerof excellence of advanced materials and processing ceamp , school of metallurgy and materialsengineering, iran university of science amp;amp; technology iust , tehran, iran


s نوری | s nouri
school of metallurgy and materials engineering, iran university of science amp;amp; technology iust , tehran, iran
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-98&slc_lang=en&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات