عنوان انگلیسی EVALUATION OFDISLOCATION STRUCTURE AND CRYSTALLITE SIZE IN WORN AL-SI ALLOY BY X-RAY DIFFRACTION
چکیده انگلیسی مقاله Abstract: powerful method for the characterization of microstructures of crystalline materials in terms of crystallite size anddislocation structures. In this paper the effect of the sliding on the microstructure of A356 in the as-cast and heattreated conditions are studied, The X-ray phase analysis shows that with increasing applied load, the dislocationdensity is increased, whereas the crystallite size is decreased. It was found that heat treatment raised dislocationdensity during wear. The screw or edge character of dislocations in worn specimens were determined by analyzing thedislocation contrast factors, it was demonstrated that the character of the prevailing dislocations in high loads isnearly pure screw.Diffraction peak profile analysis has recently been developed to such an extent that it can be applied as a
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a رضوانی فر | a rezvanifar


مرتضی زند رحیمی | m zandrahimi


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-118&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات