Iranian Journal of Materials Science and Engineering، جلد ۹، شماره ۱، صفحات ۴۲-۵۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی THE INFLUENCE OF DRY SLIDING ON PRCIPITATION HARDENING BEHAVIORS OF Al-Cu-Si ALLOY
چکیده انگلیسی مقاله Abstract: Cold working performed before an aging treatment has a significant effect on size and amount of precipitate produced. This could be caused by the increase in defect density, such as vacancies and dislocations. In this research, the Al-Cu-Si alloy was solution-treated, wear-tested and then artificially aged for a period of 1–5 h. Changes in the amount of precipitate, in the lattice parameter of the matrix, and in the precipitates are measured by X-ray diffraction and then calculated.It was observed that performing a wear test before the aging treatment was done significantly increased the amount of precipitate, while wear rate decreased.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله مرتضی زند رحیمی | m zandrahimi
department of materials science and engineering, shahidbahonar university of kerman, kerman, iran.


a رضوانی فر | a rezvanifar
department of materials science and engineering, shahidbahonar university of kerman, kerman, iran.
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-5&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات