عنوان انگلیسی EFFECT OF SUBSTRATE TEXTURE AND DEPOSITION CURRENT DENSITY ON PROPERTIES OF NiNANOCRYSTALLINE ELECTRODEPOSITS
چکیده انگلیسی مقاله Abstract: Nickel was electrodeposited onto copper substrates with high {111} and {400} peak intensities. The grain size of coatings deposited onto the copper substrate with a higher {111} peak intensity was finer. Spheroidized pyramid morphology was obtained at low current densities on both copper substrates. By increasing the deposition current density, grain size of the coating was increased for both substrates and eventually a mixed morphology of pyramids and blocks was appeared without further increase in grain size. This decreased the anodic exchange current density probably due to the decrease of surface roughness and led to a lower corrosion rate.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m r زمان زاد قویدل | m r zamanzad ghavidel


کیوان رییسی | k raeissi


احمد ساعتچی | a saatchi


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-164&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات