Iranian Journal of Materials Science and Engineering، جلد ۹، شماره ۳، صفحات ۵۸-۶۶
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی An Experimental and Theoretical Investigation of Corrosion Mechanism in a Metallic Stack
چکیده انگلیسی مقاله This paper presents an experimental and theoretical investigation of the causes of corrosion of stack in a cement plant. In this paper, information related to metallic stack failures are given in the form of a case study in Neka Cement Plant, Mazandaran, Iran. Heavy corrosion attacks were observed on the samples of stack. The failure can be caused by one or more modes such as overheating, stress corrosion cracking (SCC), hydrogen embrittlement, creep, flame impingement, sulfide attack, weld attack, dew point corrosion, etc. Theoretical calculations and experimental observations revealed that, the corrosion had taken place due to the condensation of acidic flue gases in the interior of stack. Also, the chemical analysis of the corrosion deposits and condensates confirmed the presence of highly acidic environment consisting of mostly sulfate ions.
کلیدواژه‌های انگلیسی مقاله Acid Solutions, Corrosion, Stack, Dew point, Low alloy steel
نویسندگان مقاله محمدرضا سرمستی امامی | mohammad reza sarmasti emami
iran-mazandaran-behshahr_iran university, behshahr branch
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-509-1&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سطح پوشش و خوردگی
نوع مقاله منتشر شده technical note
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات