Iranian Journal of Materials Science and Engineering، جلد ۱۰، شماره ۲، صفحات ۲۹-۳۶

عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله

عنوان انگلیسی INVESTIGATION NITRIDE LAYERS AND PROPERTIES SURFACES ON PULSED PLASMA NITRIDED HOT WORKING STEEL AISI H13
چکیده انگلیسی مقاله Nitriding is a surface treatment technique used to introduce nitrogen into metallic materials to improve their surface hardness, mechanical properties, wear resistance and corrosion resistance. In this research, the effects of plasma nitriding parameters including frequency and duty cycle were investigated on samples with different grooves dimensions. Steel blocks prepared from DIN1.2344 hot working steel were plasma nitride at 500 °C under the atmosphere contents of %75H2-%25N2, the duty cycles of 40%, 60%, 80%, and the frequencies of 8, 10 kHz for 5 hours. Then characteristics and micro hardness's of the nitrided samples were investigated using SEM, XRD, and Vickers Micro Hardness method. The results of the experiments indicated that with increasing frequency, the duty cycle, and the thickness of the grooves, the roughness of the surfaces increased. With an increase in duty cycle from 40% to 80%, the hardness of the surface rose and the thickness of the compound layer built up. Hollow cathode effect occurred in the samples with small grooves and high duty cycle in plasma nitriding. This will result in over heating of the sample which leads to a decrease in the slope of hardness values from the surface to the core of the sample and also a decrease in the diffused depth of nitrogen. The compound layer of the treated samples consisted of @ : Fe4N and : Fe2-3N phases and the proportion of the A to @ increased with the decrease in the duty cycle. Increasing the frequency did not affect the proportion of phases and micro hardness of the samples.
کلیدواژه‌های انگلیسی مقاله

نویسندگان مقاله k طاهرخانی | k taherkhani
department of mining and metallurgical engineering, amirkabir university of technology,tehran, iran

سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

f محبوبی | f mahboubi
department of mining and metallurgical engineering, amirkabir university of technology,tehran, iran

سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-18&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات