عنوان انگلیسی EFFECT OF SPIRAL DESIGN ON CRYSTAL ORIENTATION DURING SINGLE CRYSTAL GROWTH
چکیده انگلیسی مقاله Geometrical design of the spiral crystal selector can affect crystal orientation in the final single crystal structure. To achieve a better understanding of conditions associated with the onset of crystal orientation in a spiral crystal selector, temperature field was investigated using three-dimensional finite element method during the process. Different geometries of spiral crystal selector were used to produce Al- 3 wt. % Cu alloy single crystal using a Bridgman type furnace. The Crystal orientation of the samples was determined using electron backscattered diffraction (EBSD) and optical microscopy. Analysing the temperature field in the crystal selector revealed that, the orientation of growing dendrites against liquidus isotherm in the spiral selector was the reason for crystal misorientation which differs in various selector geometries. Increasing the take-off angle from 35° up to 45° increases the misorientation with respect to < 001> direction. Further increase of take-off angle greater than 45° will decrease the crystal misorientation again and the efficiency of the selector to produce a single grain is decreased.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله قنبری | m ghanbari
school of metallurgy and materials engineering, iran university of science and technology, iran, tehran

سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

محمد رضا ابوطالبی | m r aboutalebi
center of excellence for high strength alloys technology, school of metallurgy and materials engineering, iran university of science and technology, iran, tehran.

سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

s g شبستری | s g shabestari
center of excellence for high strength alloys technology, school of metallurgy and materials engineering, iran university of science and technology, iran, tehran.

سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-51&slc_lang=en&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات