عنوان انگلیسی DENSIFICATION AND MICROSTRUCTURE CHARACTERISTICS OF A PREALLOYED ALPHA BRASS POWDER PROCESSED BY LIQUID PHASE SINTERING
چکیده انگلیسی مقاله The rapidly solidified prealloyed alpha brass powder with a size range of 40 to 100 μm produced by water atomization process was consolidated using liquid phase sintering process. The relationships between sintering temperature, physic-mechanical properties and microstructural characteristics were investigated. Maximum densification was obtained at 930 °C, under 600 MPa compacting pressure, with 60 min holding time. The microstructure of the sintered brass was influenced by dezincification and structural coarsening during supersolidus liquid phase sintering. As a consequence of Kirkendall effect atomic motion between Cu and Zn atoms caused to dezincification at the grain boundaries and formation of ZnO particles on the pore surfaces. It was concluded that microstructural analysis is in a well agreement with obtained physical and mechanical properties. Also, the amount of liquid phase, which depends on sintering temperature, results in different load bearing cross section areas, and it affects the type of fracture morphologies.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a محمدزاده | a. mohammadzadeh
department of materials engineering, sahand university of technology, tabriz, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

a صباحی نمینی | a sabahi namini
department of materials engineering, sahand university of technology, tabriz, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

m آزادبه | m. azadbeh
department of materials engineering, sahand university of technology, tabriz, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-193&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات