عنوان انگلیسی DEVELOPMENT OF HARDNESS IN A Fe- BASED NANO-COMPOSITE ALLOY
چکیده انگلیسی مقاله Achieving extreme hardness in the newly synthetic steel formed by converting from initial amorphous state to subse-quent crystalline structure –named as devitrification process- was studied in this research work. Results of TEM observa-tions and XRD tests showed that crystallized microstructure were made up four different nano-scale phases i.e., α-Fe, Fe 36 Cr12 Mo10 , Fe 3 C and Fe3 B. More, Vickers hardness testing revealed a maximum hardness of 18.6 GPa which is signifi-cantly harder than existing hardmetals. Detailed kinetic and structural studies have been proof that two key factors were contributed to achieve this extreme hardness supersaturation of transition metal alloying elements (especially Nb) and also reduction in the structure to the nano-size crystals.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله s احمدی | s ahmadi
materials and biomaterials research center, biomaterials group, tehran, iran.


حمیدرضا شاهوردی | h r shahverdi
tarbiat modares university, faculty of engineering, department of materials engineering, tehran, iran.

سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-60&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات