Iranian Journal of Materials Science and Engineering، جلد ۱۱، شماره ۴، صفحات ۲۰-۲۷
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی PHASE STABILITY AND SEMICONDUCTING BEHAVIOUR OF LOW ACTIVATION AUSTENITIC MN-CR STEELS
چکیده انگلیسی مقاله Four compositions of austenitic Mn-Cr steels have been developed successfully for in-vessel component materials in power plant industry. The phase stability of these Mn-Cr steels was studied by and X-ray diffraction (XRD) patterns. XRD patterns have shown that the matrix of these Mn-Cr steels is a single γ-phase structure. The potentiodynamic polarisation curves suggested that these fabricated Mn-Cr steels showed passive behaviour in 0.1M H2SO 4solution. Therefore, semiconducting behaviour of passive film formed on these fabricated Mn-Cr steels in 0.1M H2SO 4 solution was evaluated by Mott–Schottky analysis. This analysis revealed that passive films behave as n-type and p-type semiconductors. Based on the Mott–Schottky analysis, it was also shown that donor and acceptor densities are in the order of 1021 cm -3 and are comparable for other austenitic stainless steels in acidic environments
کلیدواژه‌های انگلیسی مقاله Low activation, Mn-Cr steel, XRD, Mott–Schottky
نویسندگان مقاله a فتاح الحسینی | a fattah alhosseini
faculty of engineering, bu-ali sina university, hamedan, iran.

سازمان اصلی تایید شده: دانشگاه بوعلی سینا (Bu ali sina university)

m اسدی اسدآباد | m asadi asadabad
materials research school, nuclear science and technology research institute, isfahan, iran.
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-59&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات