عنوان انگلیسی ALUMINOTHERMIC-CARBOTHERMAL REDUCTION SYNTHESIS OF NANO CRYSTALLINE Al2O3-Ti(C,N) COMPOSITE WITH DIFFERENT BED TYPES
چکیده انگلیسی مقاله Ceramic-matrix composites containing TiC-TiN have been used in a variety of application because of their superior properties such as high hardness, good wear resistance and high chemical stability. In this research, effect of coke and coke/calcium beds in synthesis of Al 2O3-Ti(C, N) composites using alumino-carbothermic reduction of TiO 2 has been investigated. Al, TiO 2 and active carbon with additives of extra carbon and NaCl and without additives, in separate procedures, have been mixed. Afterwards, mixtures were pressed and synthesized in 1200oC for 4hrs, in coke and coke/calcium beds, separately. Al 2O3-Ti(C,N) composite was synthesized in ternary system of Al-TiO 2 -C with excess carbon and NaCl additives in calcium/coke bed in 1200 . X-ray diffraction patterns (XRD) results showed that existence of calcium in bed resulted in intensification of reduction atmosphere in samples and formation of Ti(C,N) phase enriched from carbon was accelerated. Crystallite sizes of synthesis Ti(C,N) at 1200 °C in reducing conditions were 22-28 nm.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m حیدری نسب | m heydari nasab
department of material engineering, science and research branch, islamic azad university, tehran, iran.

سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

r نقی زاده | r. naghizadeh
school of metallurgy amp;amp; materials engineering, iran university of science and technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

h صمدی | h. samadi
department of material engineering, science and research branch, islamic azad university, tehran, iran.

سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

a نعمتی | a. nemati
department of material science and engineering, sharif university of technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی شریف (Sharif university of technology)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-78&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات