Iranian Journal of Materials Science and Engineering، جلد ۱۲، شماره ۱، صفحات ۲۸-۳۴
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی COMBUSTION PERFORMANCE OF Ni-COATED AND UNCOATED HIGH ENERGETIC ALUMINUM NANOPARTICLES
چکیده انگلیسی مقاله High energetic aluminum nanoparticles are mainly used as additive in solid rocket propellants. However, fabrication of these aluminized energetic materials is associated with decreasing the burning rate of propellants due to problems such as oxidation and agglomeration of nanoparticles. In this study, to improve combustion performance of aluminum nanoparticles, coating by metallic Ni shell was studied. Nickel coating of aluminum nanoparticles was performed through electroless deposition (ED) subsequently, morphology and chemical composition of Ni-coated nanoparticles were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). These studies show that a uniform Ni layer with a thickness of 10nm is coated on the surface of Al nanoparticles. Thermal analysis of uncoated and Ni-coated aluminum nanoparticles was done using differential thermal analysis (DTA) and thermo gravimetric analysis (TGA). The results of thermal analysis indicate that, coating the aluminum particles by Ni, leads to improvement in combustion performance of aluminum nanoparticles through decreasing critical ignition temperature, ignition delay time of the nanoparticles and promoting the ignition by exothermic chemical reactions between Al and Ni
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله h شالچیان | h. shalchian
department of materials science and engineering, engineering faculty, ferdowsi university of mashhad,mashhad, iran.

سازمان اصلی تایید شده: دانشگاه فردوسی (Ferdowsi university)

a فربد | a. farbod
chemical engineering department, sahand university of technology, tabriz, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

h بیگی | h. beygi
department of materials science and engineering, engineering faculty, ferdowsi university of mashhad,mashhad, iran.

سازمان اصلی تایید شده: دانشگاه فردوسی (Ferdowsi university)

سید علی سجادی | s a sajjadi
department of materials science and engineering, engineering faculty, ferdowsi university of mashhad,mashhad, iran.

سازمان اصلی تایید شده: دانشگاه فردوسی (Ferdowsi university)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-73&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات